High efficient phosphor-converted light emitting diode

ABSTRACT

A light-emitting device and manufacturing method thereof are disclosed. The light-emitting device includes a substrate, a semiconductor light-emitting structure, a filter layer, and a fluorescent conversion layer. The method comprises forming a semiconductor light-emitting structure over a substrate, forming a filter layer over the semiconductor light-emitting structure, and forming a fluorescent conversion layer over the filter layer.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a Continuation of U.S. application Ser. No. 12/764,436 filed on Apr. 21, 2010 which was a Continuation of U.S. application Ser. No. 11/822,181, filed on Jul. 3, 2007, and for which priority is claimed under 35 U.S.C. §120; and this application claims priority of Application No. 095124433 filed in Taiwan, R.O.C. on Jul. 5, 2006 under 35 U.S.C. §119; the entire contents of which are hereby incorporated by reference.

TECHNICAL FIELD

This present disclosure relates to a light-emitting device and a method of forming the same, especially has a filter layer and a fluorescent conversion layer.

BACKGROUND OF THE DISCLOSURE

The white light LED (Light-emitting diode, LED) technology can be divided into single-chip type and multiple-chips type. The multiple-chips type using LEDs of three colors to mix the light emitted respectively into the white light. The benefit of the multiple-chips type is the flexibility of the light mixing based on different visual demand. However, the cost is relatively high for using many of LEDs chips at the same time. Furthermore, because the materials of making the LEDs with various colors are different, which needs different forward voltage (Vf) of the input, three sets of control circuit are needed. In addition, the speed of decay, the temperature characteristics and the life-time of the three kinds of LED chips are not the same, so the color of the white light is not stable and changes with time.

For single-chip type, there are three ways to manufacture the commercialized white light LED: 1. Blue LED chips combine with the yellow phosphor: The yellow phosphor used mainly is YAG phosphor of the yttrium aluminum garnet structure. The yellow light converted by the phosphor mixed with the unabsorbed blue light emitted from the blue LED can generate the white light. 2. Blue LED chips combine with the red and green phosphors: The phosphor used here is mainly containing sulfur. The red and green lights from the phosphor are combined with the unabsorbed blue light, and a white light is generated. 3. Ultraviolet LED chips combine with the red, blue and green phosphors: The ultraviolet light generated by the UV LED chips excites three or more kinds of phosphors which can respectively generates the light of red, blue and green at the same time, and the mixture of the lights mentioned above can generate the white light. To manufacture the above-mentioned devices, the phosphor and silicone is disposed into a concave after being mixed. However, it is difficult to mix the phosphor and silicone uniformly. As a result, the color temperature is uneven. When the light enters the phosphor-silicone layer from the LED, a high proportion (for example greater than 30%) of light can be back-scattered into the chips by the phosphor. Therefore, the light utilization efficiency is reduced.

U.S. Pat. No. 6,642,652 disclosed a flip-chip semiconductor light-emitting device covered by the phosphor structure formed by electrophoresis. But the method is difficult to distribute the powder uniformly in chip scale by controlling the electric field distribution and the electric charged state of the inorganic powder body, especially in the chip sidewall.

SUMMARY OF THE DISCLOSURE

This disclosure disclosed a light-emitting device and a method of forming the same. A phosphor layer is formed on the chip before encapsulation in order to avoid the disadvantage of above-mentioned known technology. Another purpose of the disclosure is to form a filter layer between LED and a fluorescent conversion layer to reduce the light luminescence efficiency loss from the LED and phosphor material stacking structure, and to improve the overall light luminescence efficiency of the device.

The light-emitting device of this disclosure includes a semiconductor structure with an active layer over a substrate, which can emit the first wavelength light; a fluorescent conversion layer over the semiconductor structure, which can absorb the first wavelength light emitted form the active layer of the semiconductor structure and can transfer the light into a second wavelength light; and a filter layer between the semiconductor structure and the fluorescent conversion layer, which has a light transmissivity of more than 50% to the first wavelength light and has a light reflectivity of more than 50% to the second wavelength light. Therefore, it can reduce the light luminescence efficiency loss caused by the absorption of the light which is back-scattered into the chip again during the transforming of the first wavelength light to the second wavelength light.

The filter layer of the light-emitting device of this disclosure is formed by one kind of material, or stacking or mixing two or more kind of materials. Such material has wavelength selectivity, which has a light transmissivity of more than 90% and lower light reflectivity to the ultraviolet light, or has a light transmissivity of lower than 5% and higher light reflectivity to the visible light.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing aspects and many of the attendant advantages of this disclosure are more readily appreciated as the same becomes better understood by reference to the following detailed description, when taken in conjunction with the accompanying drawings, wherein:

FIG. 1 is a schematic view of the first embodiment of the present disclosure.

FIG. 2 is a reflectivity spectrum of the filter layer that is made by TiO₂ and SiO₂ in the first embodiment of the present disclosure.

FIG. 3 is a schematic view of the second embodiment of the present disclosure.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

FIG. 1 shows a schematic view of the preferred embodiment of the present disclosure. The disclosure discloses a light-emitting device 10 comprising a substrate 11, a semiconductor layer 12 having an active layer to emit a first wavelength light, a filter layer 13 and a fluorescent conversion layer 14. The material of the substrate 11 is composed of either opaque material or transparent material. For opaque material, it can be semiconductor metal or other opaque materials. In a preferred embodiment, the material of the substrate is selected from the group of Si, GaN/Si, GaAs and the combination of the above materials. For transparent materials, it can be glass, sapphire, SiC, GaP, GaAsP, ZnSe, ZnS or ZnSSe. The structure of the semiconductor structure 12 is either vertical (the electrical contacts located on the different side of the structure) or horizontal (the electrical contacts located on the same side of the structure). When the first wavelength light passes the filter layer 13 and enters the fluorescent conversion layer 14, it is absorbed and converted into a second wavelength light. The unabsorbed first wavelength light is mixed with the second wavelength light and a white light is generated consequently.

In addition, as FIG. 1 shows, more than two semiconductor structures 12 are formed by forming a trench 1202 on the substrate, and then a plurality of chips are formed by dicing process. The dicing process can also be performed after forming the filter layer 13 and the fluorescent conversion layer 14.

A filter layer 13 is stacked by at least two materials with different refractive indexes and is formed on the semiconductor structure 12 by deposition process. The average light reflectivity is greater than 90% to the visible light. A preferred selection of the combination of the at least two materials with different refractive indexes is a higher refractive material with a refractive index of 2.1 to 2.6, such as TiO₂, Nb₂O₅ or Ta₂O₅, and a lower refractive material with a refractive index of 1.2 to 1.6, such as SiO₂ or MgF₂. The thickness of the filter layer is in the range from several tens of angstroms to several tens of micrometers, depending on the material characteristic. The filter layer can almost allow the whole transmission of the ultraviolet light. FIG. 2 shows a reflectivity spectrum of the filter layer that is made by TiO₂ and SiO₂.

A fluorescent conversion layer 14 is formed on the filter layer 13, and its forming method comprises the following steps:

(1) Surface modification of the fluorescent conversion material: Taking 0.3 gram of Yttrium Aluminum Garnet (YAG) phosphor and 5 ml of γ-3-glycidoxypropylimethoxymethylsilane mixed with 30 ml of 95% (volume percentage) alcoholic solution. After heating the mixed solution to 70° C. and stirring for 2 hours, the powder in the solution is filtered out. Washing the powder with alcohol and drying it at 85° C., then a surface modified of the YAG phosphor. (2) Formation of the fluorescent conversion material: Mixing the surface modified the YAG phosphor with the Isopropanol, then pouring them into the container with a wafer inside, waiting for the YAG phosphor powder deposited on the wafer surface by the gravity and leaving the upper solution clear. Distilling most of the upper clear solution, and then put the container into the oven with a temperature of 120° C. to form the fluorescent conversion material by baking YAG phosphor. (3) Protection of the fluorescent conversion material: To survive the following light-emitting device manufacturing processes, the fluorescent conversion material must be anticorrosive and have strong adhesion. Using the hardened resin with the low viscosity and the high impermeability of ultraviolet light to form a film on the surface of the YAG fluorescent conversion layer can protect the device effectively.

The substrate 11 and the semiconductor structure 12 are electrically connected and then are diced to produce the light-emitting diode chips having a filter layer and a fluorescent conversion layer.

FIG. 3 shows a schematic view of another preferred embodiment of the present disclosure. The numerals of the elements in this embodiment are the same as the elements in the first embodiment. The light-emitting device 20 structure and its manufacturing method are the same as the above-mentioned also. After forming the semiconductor structure 12 having an active layer, a first filter layer 1301 is then deposited on the active layer. Depositing a fluorescent conversion layer 14 on the first filter layer 1301, and depositing a second filter layer 1302 on the fluorescent conversion layer 14 finally. The first filter layer 1301 has a light transmissivity of more than 50% to the first wavelength light and a light reflectivity of more than 50% to the second wavelength light. The second filter layer 1302 has a light reflectivity of more than 50% to the first wavelength light and has a light transmissivity of more than 50% to the second wavelength light.

The first filter layer 1301 is stacked by at least two materials with different refractive indexes. The at least two materials can almost allow the whole transmission to the ultraviolet light, and the average reflectivity of the materials is above 90% to the visible light (400 nm≦λ≦700 nm). The second filter layer 1302 is stacked by at least two materials with different refractive indexes. The average reflectivity of the materials is near 100% to the ultraviolet light, and is very low (≦1%) to the visible light. A preferred selection of the combination of the at least two materials with different refractive indexes is a higher refractive material with a refractive index of 2.1 to 2.6, such as TiO₂, Nb₂O₅ or Ta₂O₅, and a lower refractive material with a refractive index of 1.2 to 1.6, such as SiO₂ or MgF₂. The thicknesses of the filter layers are in the range from several tens of angstroms to several tens of micrometers depending on the material characteristic.

The embodiment includes a layer structure comprising, a conversion layer adapted to emit a second wavelength light in response to a first wavelength light coming from an outside of the layer structure; a first layer having a light reflectivity of more than 50% to the second wavelength light, and separate from the conversion layer by a first boundary; a second layer having a light transmissivity of more than 50% to the second wavelength light, and separated from the conversion layer by a second boundary being longer than the first boundary. The conversion layer comprises a phosphor.

Although specific embodiments have been illustrated and described, it will be apparent that various modifications may fall within the scope of the appended claims. 

1. A layer structure, comprising: a conversion layer adapted to emit a second wavelength light in response to a first wavelength light coming from an outside of the layer structure; a first layer having a light reflectivity of more than 50% to the second wavelength light, and separated from the conversion layer by a first boundary; a second layer having a light transmissivity of more than 50% to the second wavelength light, and separated from the conversion layer by a second boundary being longer than the first boundary.
 2. The layer structure of claim 1, wherein the first layer has a light transmissivity of more than 50% to the first wavelength light.
 3. The layer structure of claim 1, wherein the conversion layer comprises a phosphor.
 4. The layer structure of claim 1, wherein the first layer or the second layer comprises a lower refractive material and a higher refractive material.
 5. The layer structure of claim 1, wherein the first layer comprises a refractive material having a refractive index of 1.2 to 1.6 or 2.1 to 2.6.
 6. The layer structure of claim 1, wherein the first wavelength light is adapted to mix with the second wavelength light in order to produce a white light.
 7. The layer structure of claim 1, wherein the first boundary is substantially parallel to the second boundary.
 8. A layer structure, comprising: a conversion layer adapted to absorb a first wavelength light and emit a second wavelength light; a first layer having a light reflectivity of more than 50% to the second wavelength light, and contacting the conversion layer with a first boundary; a second layer having a light transmissivity of more than 50% to the second wavelength light, and contacting the conversion layer with a second boundary being longer than the first boundary.
 9. The layer structure of claim 8, wherein the first layer has a light transmissivity of more than 50% to the first wavelength light.
 10. The layer structure of claim 8, wherein the conversion layer comprises a phosphor.
 11. The layer structure of claim 8, wherein the first layer or the second layer comprises a lower refractive material and a higher refractive material.
 12. The layer structure of claim 8, wherein the first layer comprises a refractive material having a refractive index of 1.2 to 1.6 or 2.1 to 2.6.
 13. The layer structure of claim 8, wherein the first boundary is substantially parallel to the second boundary.
 14. The layer structure of claim 8, wherein the first wavelength light is adapted to mix with the second wavelength light in order to produce a white light.
 15. A layer structure, comprising: a conversion layer adapted to emit a converted light and an unabsorbed light; a first layer having an average reflectivity of above 90% to a visible light, and separated from the conversion layer by a first boundary; a second layer separated from the conversion layer by a second boundary being longer than the first boundary.
 16. The layer structure of claim 15, wherein the second layer having a light transmissivity of more than 50% to the converted light
 17. The layer structure of claim 15, wherein the converted light is adapted to mix with the unabsorbed light in order to produce a white light.
 18. The layer structure of claim 15, wherein the visible light is between 400 nm and 700 nm.
 19. The layer structure of claim 15, wherein the first layer or the second layer comprises a lower refractive material and a higher refractive material.
 20. The layer structure of claim 15, wherein the first boundary is substantially parallel to the second boundary. 